Journal
TRIBOLOGY INTERNATIONAL
Volume 177, Issue -, Pages -Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.triboint.2022.107972
Keywords
Inconel 718; Abrasive belt grinding; Wear mechanism; Surface integrity
Categories
Ask authors/readers for more resources
This study uses electroplated diamond abrasive belts (EDAB) to grind Inconel718. It is found that EDAB shows stable grinding performance, and the wear mechanism in different wear stages is primarily micro cleavage fracture, macro cleavage fracture, and adhesive wear. With the wear of EDAB, the surface roughness decreases and reaches a minimum of Ra0.5μm, and the subsurface crystalline grains of Inconel718 are refined. Furthermore, the use of low-hardness contact wheels significantly reduces abrasive belt wear and improves surface integrity.
Serious wear can easily occur in traditional abrasive belts during grinding nickel-based superalloy components. To find an abrasive belt with excellent wear resistance and surface finishing, this study uses electroplated diamond abrasive belt (EDAB) to grind Inconel718, and investigates its wear evolution and corresponding grinding surface integrity. It was revealed that EDAB showed stable grinding performance, and the wear mechanism in initial, steady, and final wear stage was primarily micro cleavage fracture, macro cleavage fracture and adhesive wear, respectively. As EDAB wore, ground surface roughness gradually decreased and reached a minimum of Ra0.5 mu m, and subsurface crystalline grains of Inconel718 were refined. Furthermore, the abrasive belt wear was significantly reduced and the surface integrity was improved using low-hardness contact wheels.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available