The Multi-Step Chain Extension for Waterborne Polyurethane Binder of Para-Aramid Fabrics

The comprehensive balance of the mechanical, interfacial, and environmental requirements of waterborne polyurethane (WPU) has proved challenging, but crucial in the specific application as the binder for high-performance polymer fiber composites. In this work, a multi-step chain extension (MCE) method was demonstrated using three kinds of small extenders and one kind of macro-chain extender (CE) for different chain extension steps. One dihydroxyl blocked small molecular urea (1,3-dimethylolurea, DMU) was applied as one of the CEs and, through the hybrid macrodiol/diamine systems of polyether, polyester, and polysiloxane, the WPU was developed by the step-by-step optimization on each chain extending reaction via the characterization on the H-bonding association, microphase separation, and mechanical properties. The best performance was achieved when the ratio of polyether/polyester was controlled at 6:4, while 2% of DMU and 1% of polysiloxane diamine was incorporated in the third and fourth chain extension steps, respectively. Under the condition, the WPU exhibited not only excellent tensile strength of 30 MPa, elongation of break of about 1300%, and hydrophobicity indicated by the water contact angle of 98 degrees, but also effective interfacial adhesion to para-aramid fabrics. The peeling strength of the joint based on the polysiloxane incorporated WPU after four steps of chain extension was 430% higher than that prepared through only two steps of chain extension. Moreover, about 44% of the peeling strength was sustained after the joint had been boiling for 40 min in water, suggesting the potential application for high-performance fabric composites.

Automated summary

This study developed a high-performance waterborne polyurethane (WPU) as a binder for polymer fiber composites using a multi-step chain extension method. By optimizing the chain extending reaction, the WPU exhibited excellent mechanical properties, suitable interfacial adhesion, and potential application for high-performance fabric composites.