Gold nanoparticles deposited on Amberlyst-15: Metal-acid bifunctional catalyst for cellobiose conversion to gluconic acid

Gold nanoparticles were deposited on two kinds of solid acids, i.e., amorphous SiO2-Al2O3 and cation-exchange resin Amberlyst-15; the resultant materials exhibited high activity as metal-acid bifunctional catalysts. SiO2-Al2O3 was impregnated with a chloride-free alkaline Au(III) solution containing Na+ and then dried. After calcination at 623 K, gold nanoparticles with diameters of 4.2 nm (measured by X-ray diffraction) were deposited at a Au loading of 1.0 wt%. By replacing the Na+ ions with 1-1(+) ions through ammonium ion-exchange and heating, an acidic Au/SiO2-Al2O3 catalyst was obtained. In Amberlyst-15, gold nanoparticles with diameters of 7.3 nm were deposited after impregnation and drying. Subsequent ion-exchange with dilute sulfuric acid generated the acidic form of the Au/Amberlyst-15 catalyst, which showed an esterification activity equivalent to that of the original Amberlyst-15. The catalyst exhibited high activity for the direct conversion of cellobiose to gluconic acid, which requires both acid hydrolysis and oxidation. A 45% yield of gluconic acid was obtained after 24 h of reaction under ambient air at 373 K, with an apparent synergistic effect between the gold nanoparticles and acidic resin surface. (C) 2014 Elsevier B.V. All rights reserved.