Fouling characterisation in PVDF membrane contactors for dissolved methane recovery from anaerobic effluents: effect of surface organofluorosilanisation

Journal

ENVIRONMENTAL SCIENCE AND POLLUTION RESEARCH
Volume 30, Issue 11, Pages 29164-29179

Publisher

SPRINGER HEIDELBERG
DOI: 10.1007/s11356-022-24019-z

Keywords

Fluoroalkylsilane; Hydrophobic membrane; Membrane fouling; Membrane stability; PVDF flat-sheet; Surface functionalisation

Ask authors/readers for more resources

The fouling attached to PVDF membranes treating anaerobic effluent for dissolved CH4 recovery was characterized. Both organic and inorganic fouling were observed, with proteins, polysaccharides, and calcium and phosphate salts as the main foulants. The mPVDF membrane suffered more severe fouling and had lower stability. The fouling exhibited a stratification on the membrane and irreversible fouling remained after extraction.
Characterisation of the fouling attached to PVDF membranes treating an anaerobic effluent for dissolved CH4 recovery was carried out. A commercial flat- sheet PVDF membrane and a PVDF functionalised by grafting of organofluorosilanes (mPVDF) that increased its hydrophobicity were subjected to a continuous flux of an anaerobic reactor effluent in long-term operation tests (> 800 h). The fouling cakes were studied by the membrane autopsy after these tests, combining a staining technique, FTIR, and FESEM-EDX, and the fouling extraction with water and NaOH solutions. Both organic and inorganic fouling were observed, and the main foulants were proteins, polysaccharides, and different calcium and phosphate salts. Also, a significant amount of live cells was detected on the fouling cake (especially on the non-modified PVDF). Although the fouling cake composition was quite heterogeneous, a stratification was observed, with the inorganic fouling mainly in the bulk centre of the cake and the organic fouling mainly located in the lower and upper surfaces of the cake. The mPVDF suffered a more severe fouling, likely owing to a stronger hydrophobic-hydrophobic interaction with the foulants. Irreversible fouling remained on both membranes after the extraction, although a higher irreversible fouling was detected in the mPVDF; however, a complete polysaccharide removal was observed. Regarding the operation performance, PVDF showed a lower stability and suffered a severe degradation, resulting in a lower thickness and perforations. Finally, the decrease in the methane recovery performance of both membranes was associated with the fouling depositions.

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.7
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available