Heating influence on hierarchical structures fabricated by direct laser interference patterning

The combination of direct laser interference patterning (DLIP) with laser-induced periodic surface structures (LIPSS) enables the fabrication of functional surfaces reported for a wide spectrum of materials. The process throughput is usually increased by applying higher average laser powers. However, this causes heat accumulation impacting the roughness and shape of produced surface patterns. Consequently, the effect of substrate temperature on the topography of fabricated features requires detailed investigations. In this study, steel surfaces were structured with line-like patterns by ps-DLIP at 532 nm. To investigate the influence of substrate temperature on the resulting topography, a heating plate was used to adjust the temperature. Heating to 250 degrees C led to a significant reduction of the produced structure depths, from 2.33 to 1.06 mu m. The reduction is associated with the appearance of a different LIPSS type, depending on the grain orientation of the substrates and laser-induced superficial oxidation. This study revealed a strong effect of substrate temperature, which is also to be expected when heat accumulation effects arise from processing surfaces at high average laser power.

Automated summary

The study revealed that adjusting the substrate temperature can significantly impact the structure depth and morphology of steel surfaces, resulting in different types of LIPSS being produced.