TEXTILE RESEARCH JOURNAL
Volume 93, Issue 7-8, Pages 1686-1698Publisher
SAGE PUBLICATIONS LTD
DOI: 10.1177/00405175221134974
Keywords
Modified nano-ZnO; organic fluorosilicone; linen fabric; antibacterial property; hydrophobic property
Categories
Ask authors/readers for more resources
Textile research is driven by economy and functionality, and current research focuses on developing multifunctional textiles with simple processes. In this study, a highly efficient multifunctional linen fabric finishing agent was developed using nano-ZnO and various raw materials, providing the linen fabric with characteristics such as hydrophobicity, antibacterial properties, and ultraviolet protection. Analysis of the finishing agent's main characteristics using techniques such as infrared spectroscopy and transmission electron microscopy confirmed its successful preparation and stability. Moreover, the application performance of the finished linen fabric was tested, showing improved ultraviolet protection, antibacterial properties, hydrophobicity, washing fastness, and breaking strength compared to the original linen fabric. The multifunctional linen fabric finishing agent demonstrates advantages in terms of simplicity, cost-effectiveness, and promising prospects.
The research in textiles is being driven by economy and functionality. Therefore, the present research is focused on the development of multifunctional textiles with simple process. Herein, a highly efficient multifunctional linen fabric finishing agent was developed with nano-ZnO, dodecafluoroheptyl methacrylate, vinyl trimethoxysilane, methyl methacrylate, and butyl acrylate as raw materials. The finishing agent imparted linen fabric multiple performance characteristics such as hydrophobic, antibacterial and ultraviolet protection. Infrared spectroscopy analysis, particle size test and transmission electron microscopy were used to analyze the main characteristics of multifunctional linen fabric finishing agent, including the main groups, particle size distribution and particle morphology. The results showed that the nano-ZnO/fluorosilicone-polyacrylate emulsion finishing agent had been successfully prepared, and the finishing agent had good stability. By means of scanning electron microscopy, thermogravimetry, and X-ray diffractometry, it was found that the finishing agent successfully covered the surface of the linen fabric, which increased the thermal decomposition temperature of the linen fabric and reduced the crystallinity of the linen fabric, indicating that improved the heat stability and softness of the fabric. Similarly, the application performance of linen fabric was tested. Compared with the original linen fabric, the finished linen fabric had good ultraviolet protection, antibacterial, hydrophobicity, washing fastness and breaking strength, leading to the improvement of the wear performance of linen fabric. Thus, the multifunctional linen fabric finishing agent has the advantages of simple technology, low cost and promising prospect.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available