Mg-Gd-Y(-Sm)-Zr alloys; Constitutive equations; Dynamic recrystallization; Dynamic precipitation
Categories
Funding
- National Natural Science Foundation of China [51571084]
- Natural Science Foundation of Henan Province [222300420435]
- Central Plains Talent Program-Central Plains Youth Top Talents, China
Ask authors/readers for more resources
The deformation behavior of Mg-Gd-Y(-Sm)-Zr alloys during high-temperature uniaxial compression was investigated. The dynamic recrystallization critical strain was calculated and verified. The hot deformation activation energy and constitutive equation were calculated, and the effect of Sm on microstructure evolution was analyzed. The results showed that the addition of Sm increased flow stress and delayed dynamic recrystallization.
We investigated the deformation behavior of Mg-Gd-Y(-Sm)-Zr alloys during high-temperature uniaxial compression (T = 350 degrees C, 400 degrees C, 450 degrees C and 500 degrees C; =0.003 s-1, 0.01 s-1, 0.1 s-1 and 1 s-1). The dynamic recrystallization (DRX) critical strain of Mg-Gd-Y(-Sm)-Zr was calculated, and its accuracy was verified by the transmission electron microscope (TEM). The hot deformation activation energy and constitutive equation after hot compression were calculated. The effect mechanism of Sm on microstructure evolution was also analyzed by the electron backscatter diffraction (EBSD) and TEM. It can be concluded that the hot deformation activation energies of Mg-Gd-Y-Zr and Mg-Gd-Y-Sm-Zr were 206.17 kJ/mol and 263.07 kJ/mol, respectively. The addition of Sm can increase flow stress and make DRX occur earlier. With the increase of strain, Sm delayed the DRX by inhibiting the activity of pyramidal < c+a > slip. Under the deformation condition of 400 degrees C/0.003 s-1/0.7, the continuous dynamic recrystallization (CDRX) mechanism was domi-nant in Mg-Gd-Y-Zr and Mg-Gd-Y-Sm-Zr. In addition, the dynamic precipitation phase after adding Sm was the ss-Mg5(Gd, Y, Sm) equilibrium phase with a face-centered cubic structure. There was a staggered chain distribution between DRX grains and precipitates at the original deformation grain boundary, which effectively hinders dislocation rearrangement and grain boundary migration. Finally, we constructed the DRX mechanism diagram and the interaction diagram between the precipitated phase and DRX grains.' (c) 2022 Elsevier B.V. All rights reserved.