Super Broadband at Telecom Wavelengths From RE3+-Doped SiO2-Ta2O5 Glass Ceramics Planar Waveguides

This paper reports on the preparation of Er3+/Yb3+/Tm3+, Er3+/Yb3+/Nd3+, and Er3+/Tm3+/Nd3+ triply doped and Er3+-doped SiO2-Ta2O5 glass ceramic nanocomposites and active planar waveguides by the sol-gel process using the dip-coating technique as deposition method. The investigation of their structural, morphological, and luminescent properties using XRD, AFM, and photoluminescence analysis, are reported here. The XRD results showed the presence of L-Ta2O5 nanocrystals dispersed in the SiO2-based amorphous host for all the nanocomposites and films. The rare earth ion (RE3+) doping concentration affected both the crystallinity, and the crystallite sizes of the Ta2O5 dispersed into SiO2-Ta2O5 nanocomposites and waveguides. AFM characterization revealed crack free and smooth surface roughness and differences in viscoelasticity on the Er3+-doped SiO2-Ta2O5 films surface, which allows the identification of Ta2O5 nanocrystals on the SiO2 amorphous host. The Er3+ doped and triply doped SiO2-Ta2O5 nanocomposites displayed broad- and super broadband NIR emissions with a FWHM up to 173 nm achieved in the telecom wavelengths. The lifetime of the I-4(13/2) emitting level of the Er3+-doped SiO2-Ta2O5 waveguides is strongly dependent on Er3+ concentration and an emission quenching was negligible up to 0.81 mol%. The structural and luminescent investigations indicated that RE3+-doped SiO2-Ta2O5 glass ceramics are promising candidates for photonic applications in optical devices operating in wide wavelengths at the telecom bands.

Automated summary

This paper reports on the preparation of Er3+/Yb3+/Tm3+, Er3+/Yb3+/Nd3+, and Er3+/Tm3+/Nd3+ triply doped and Er3+-doped SiO2-Ta2O5 glass ceramic nanocomposites and active planar waveguides, and the investigation of their structural, morphological, and luminescent properties using XRD, AFM, and photoluminescence analysis. The results showed that these materials exhibited broad- and super broadband NIR emissions in the telecom wavelengths, and the rare earth ion doping concentration affected the crystallinity and crystallite sizes of the nanocomposites and waveguides.