Microstructure and Mechanical Properties of AZ91 Rein-Forced with High Volume Fraction of Oriented Short Carbon Fibers

Journal

MATERIALS
Volume 15, Issue 14, Pages -

Publisher

MDPI
DOI: 10.3390/ma15144818

Keywords

AZ91 magnesium alloy; carbon fibers; fiber orientation; squeeze casting; composite; microstructure; mechanical properties

Funding

  1. Deanship of Scientific Research at Imam Mohammad Ibn Saud Islamic University, KSA [RG-21-12-07]

Ask authors/readers for more resources

In this study, an AZ91/23 vol.% short carbon fiber composite was produced using a squeeze casting technique. The composite exhibited improved hardness, compressive strength, and wear properties compared to the AZ91 matrix. The performance of the composite was influenced by fiber orientation. The parallel composite specimen showed the highest compressive properties but the lowest ductility among the tested specimens.
In this study, AZ91/23 vol.% short carbon fiber composite was produced by a squeeze casting technique using a cylindrical pre-form of treated carbon fibers, in which the fibers are randomly oriented in the horizontal plane. Cylindrical specimens (height = 9 mm and diameter = 6 mm) were machined from the as-cast AZ91 matrix and its composite. The full behavior of the produced composite was studied through the test specimens machined in two directions, namely parallel to the reinforced plane (in the radial direction of the cast cylinder) and normal to the reinforced plane (in the axial direction of the cast composite). The microstructures of the produced composite specimens were investigated using SEM equipped with EDS analysis. Density, hardness, compressive, and wear behavior were also investigated. For comparison, the AZ91 matrix was evaluated as a reference. The microstructure of the produced AZ91 matrix alloy and its composite revealed dense materials without casting defects. Both composite specimens show improvement in hardness, compressive strength, and wear properties over the AZ91 matrix. The compressive and wear properties are more fiber orientation-dependent than the hardness results. The parallel composite specimen depicts the highest compressive properties in terms of yield compressive strength (311 MPa) and ultimate compressive strength (419 MPa), compared to that shown by the AZ91 matrix and the normal composite specimen. This improvement in compressive strength was at the expense of ductility. The parallel composite specimen shows the lowest ductility (R = 3.8%), compared to that given by the normal composite specimen (R = 7.1) and the AZ91 matrix alloy (R = 13.6). The wear testing results showed that at the highest wear load of 5 N, the material weight loss of the parallel composite specimen decreases by 44% and 64% compared to the AZ91 matrix and the normal composite specimen, respectively.

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.6
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available