Investigation of the Gamma-ray Shielding Performance of CuO-CdO-Bi2O3 Bentonite Ceramics

The purpose of this research is to identify the radiation shielding capability of ceramics adding CuO, CdO, and Bi2O3 with diverse wt (%). The chemical compositions of the raw ceramics were documented through Energy Dispersive X-ray EDX techniques. For aesthetic appeal and solidification, CuO has been chosen to be added to ceramic. Moreover, in the interest of increasing the radiation shielding ability, the high atomic number and density of both CdO and Bi2O3 were suggested for the raw ceramics. To obtain the morphological features of the prepared ceramic samples, a Scanning Electron Microscope, or SEM, was utilized. To verify the experimental results, the MCA value obtained from the Phy-X software was compared to the experimental value collected from the HPGe detector. At energies 0.06 MeV, 0.662 MeV, 1.173 MeV, and 1.333 MeV the linear and mass attenuation coefficients of the prepared ceramics have been measured using a high purity germanium HPGe detector as well as three different point sources. Moreover, the relationship between ln(I) and the thickness of the ceramics has been presented here, and the comparison between the LAC of the prepared ceramics with other materials has also been displayed. Bentonite ceramic containing CuO (15 mol %)-CdO (15 mol %)-Bi2O3 (20 mol %) with density 3.6 showed the lowest HVL, MFP, and TVL at all studied energies, yet pure Bentonite ceramic containing only CuO (50 mol %), having density 3.4, presented the greatest values. Hence, it can be concluded that the addition of CdO and Bi2O3 enhances the radiation shielding ability.

Automated summary

The purpose of this research is to investigate the radiation shielding capability of ceramics with added CuO, CdO, and Bi2O3. The chemical compositions of the ceramics were analyzed using Energy Dispersive X-ray (EDX) techniques, and the morphology of the prepared samples was observed using a Scanning Electron Microscope (SEM). The results showed that the addition of CdO and Bi2O3 enhanced the radiation shielding ability of the ceramics.