The Correlation of Surface Roughness Parameters of Zirconia and Lithium Disilicate with Steatite Wear

Purpose Various surface roughness parameters are utilized to describe the surface in the tooth to ceramics abrasion and to assess the resulting wear. The use of three-dimensional parameters may offer a better estimation for wear and an improved deduced clinical surface treatment. The aim of this study was to determine the influence of various surface roughness parameters of zirconia and lithium disilicate ceramics on the wear of steatite antagonists. Material and methods Forty zirconia specimens with a diameter of 7 mm and a thickness of 3 mm and 40 lithium disilicate specimens with the dimensions 10x10x4 mm were each divided into five subgroups. Two subgroups were treated with different clinically established diamond burs; a third subgroup was treated with a silicone polishing set. Two additional subgroups were produced by glazing the surfaces after treatment. Surface roughness parameters were determined by laser scanning microscopy. All specimens underwent 1.2 million loading cycles using steatite antagonists. After regular intervals of cycles, precision impressions were made to assess the wear. The correlation between wear and different roughness parameters was evaluated using the Spearman correlation test. Results For the glazed zirconia, unglazed zirconia, and glazed lithium disilicate specimens no significant correlations (p > 0.05) between the investigated roughness parameters and antagonist wear could be found. In the unglazed lithium disilicate groups, significant (p <= 0.05) correlations with steatite substance loss could be found for several roughness parameters after 1.2 million cycles. Conclusions For lithium disilicate, it seems not sufficient to use only one roughness parameter to indicate the wear behavior of the surface. There was no correlation between wear and the tested roughness parameters of zirconia surfaces.

Automated summary

This study aimed to determine the influence of various surface roughness parameters of zirconia and lithium disilicate ceramics on the wear of steatite antagonists. The results showed no significant correlations between the investigated roughness parameters and antagonist wear for glazed zirconia, unglazed zirconia, and glazed lithium disilicate specimens.