Initial High-Temperature Oxidation Behavior of Fe-Mn Binaries in Air: The Kinetics and Mechanism of Oxidation

Journal

OXIDATION OF METALS
Volume 98, Issue 1-2, Pages 217-237

Publisher

SPRINGER/PLENUM PUBLISHERS
DOI: 10.1007/s11085-022-10115-5

Keywords

Oxidation; Mechanism; Kinetics; TGA; Gas phase diffusion

Funding

  1. Dutch government [T17019p]

Ask authors/readers for more resources

In this study, the oxidation mechanism, affecting parameters, and linear-to-parabolic growth transition of different Fe-Mn alloys were investigated under various oxygen partial pressures and gas flow rates. The oxidation rate was found to be controlled by the diffusion of oxidizing molecules to the sample's surface.
High-temperature oxidation of steels can be relatively fast when exposed to air. Consequently, elucidating the effect of different parameters on the oxidation mechanism and kinetics is challenging. In this study, short-time oxidation was investigated to determine the oxidation mechanism, the affecting parameters, and the linear-to-parabolic growth transition of different Fe-Mn alloys in various oxygen partial pressures (10-30 kPa) and gas flow rates (26.6 and 53.3 sccm) in a temperature range of 950-1150 degrees C. Oxidation kinetics was investigated using a thermogravimetric analyzer (TGA) under controlled atmosphere. Linear oxide growth was observed within the first 20 minutes of oxidation. The linear rate constant was significantly increased by increasing the oxygen partial pressure or the flow rate of the oxidizing gas. The morphology of the oxide layer was determined by scanning electron microscopy (SEM). The crystal structure of the oxides formed was followed by in-situ X-ray diffraction (XRD), confirming that the growing layer consists of wustite mainly, which upon slow cooling to room temperature, transformed into magnetite. Energy-dispersive X-ray spectroscopy (EDS) showed that the atomic ratio of Fe+Mn to O was similar to 1.03:1 in the oxide scale, corresponding to Fe(Mn)O formation. Based on the characterization and a model for linear growth kinetics, it is concluded that the oxidation rate is controlled by the diffusion of oxidizing molecules through the gas layer to the sample's surface. The findings led to a better understanding of initial oxidation behavior and provided a pathway for improved insight into the high-temperature oxidation behavior for more complex alloys.

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.4
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available