Electrochemical detection of hydrogen peroxide using micro and nanoporous CeO2 catalysts

In this research work, focus has been made on a glassy carbon electrode (GCE) modified commercial micro and synthesized nano-CeO2 for the detection of hydrogen peroxide (H2O2). Firstly, CeO2 nanoleaves were prepared by solvothermal route. Both commercially available micro CeO2 and synthesized nano-CeO2 structures were analyzed by different characterization techniques. The Raman spectra of synthesized nano CeO2 has more oxygen vacancies than micro CeO2. SEM images revealed that the synthesized CeO2 acquired leaf-like morphology. The catalyst nano CeO2 offered mesoporosity from nitrogen adsorption-desorption isotherms with massive sites of activation for increasing efficiency. Experiments on determining H2O2 using micro CeO2 or nano-CeO2/GCE was conducted using cyclic voltammetry (CV) and amperometry. Enhanced H2O2 reduction peak current with lower potential was observed in nano-CeO2/GCE. The influence of scan rate and H2O2 concentration on the performance of nano-CeO2/GCE were also studied. The obtained results have indicated that nano-CeO2/GCE showed improved electrochemical sensing behavior towards the reduction of H2O2 than micro-CeO2/GCE and bare GCE. A linear relationship was obtained over 0.001 mu M-0.125 mu M concentration of H2O2, with good sensitivity 141.96 mu A mu M 1 and low detection limit of 0.4 nM. Hence, the present nano-CeO2 system will have a great potential with solvothermal synthesis approach in the development of electrochemical sensors.

Automated summary

This research focuses on the detection of hydrogen peroxide using a glassy carbon electrode modified with commercial micro and synthesized nano-CeO2. The nano-CeO2 exhibited improved electrochemical sensing behavior compared to the micro-CeO2 electrode. The solvothermal synthesis approach was used to prepare the nano-CeO2, which showed a leaf-like morphology and increased oxygen vacancies.