Journal
CERAMICS INTERNATIONAL
Volume 48, Issue 13, Pages 18765-18772Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2022.03.151
Keywords
Lithium energy storage; CNTs; Microspheres; Superior rate performance; Al(3+)doping; Li3V2(PO4)(3)@C
Categories
Funding
- Ministry of Education of China University Innovation Fund Project [2019YYA04001]
- Sub-project of Guangdong Provincial Science and Technology Planning Project (Foreign Science and Technology Coop-eration Platform) [2019A050520001]
- Basic and Applied Basic Research Project of Guangzhou Science and Technology Bureau [202102080264]
- College Scientific Research Project of Guangzhou Education Bureau-Innovation Team Scientific Research Project [202032848]
- Provincial Higher Education Teaching Re-form Project [2019-456]
- Guangzhou Education Science Planning Project [201911941]
- Provincial Quality Engineering Project [2019-89]
Ask authors/readers for more resources
A series of three-dimensional Al3+-doped Li3V2(PO4)(3)@C/CNTs microspheres were fabricated for the first time using a simple spray drying and solid-state reaction process. The Li+ diffusion coefficient and electrical conductivity of Li3V2(PO4)(3) were significantly enhanced due to the Al3+ doping and the formation of a three-dimensional network by the carbon film and CNTs. The Al3+-doped composites showed excellent lithium storage properties, including high capacity and good cyclic-life, making Al3+ doping a promising strategy for improving the rate properties of Li3V2(PO4)(3) for lithium energy storage.
A series of three-dimensional Al3+-doped Li3V2(PO4)(3)@C/CNTs microspheres have been fabricated for the first time using a facile spray drying route followed through a solid-state reaction process. The crystalline structure, morphology, microstructure and lithium storage performance for the fabricated composites have been researched using Raman spectrum, XRD, XPS, SEM, TEM, EDS and various electrochemical tests. Benefiting from the Al3+ doping and formed three-dimensional networks by the carbon film and CNTs, the Li+ diffusion coefficient and electrical conductivity of Li3V2(PO4)(3) are significantly enhanced. All the Al3+-doped composites possess superior lithium storage properties including high capacity and good cyclic-life. Thus, Al3+ doping is a prospective strategy to promote the rate properties of Li3V2(PO4)(3) for lithium energy storage.