Journal
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T
Volume 19, Issue -, Pages 1798-1804Publisher
ELSEVIER
DOI: 10.1016/j.jmrt.2022.05.126
Keywords
Al-Mg-Si-Mn alloy; Rare earth element; Microstructure; Mechanical properties
Funding
- National Natural Science Foundation of China [U1902220]
- Yunnan Fundamental Research Projects [202101BE070001-041, 202201AT070099]
- Science and Technology Major Project of Yunnan Province [202202AG050011, 202202AB080011]
Ask authors/readers for more resources
The effect of Ce content in the range of 0-0.5 wt.% on the microstructure and mechanical properties of squeeze-cast Al-5Mg-2.2Si-0.6Mn alloys was investigated. The addition of Ce resulted in grain refinement and improved mechanical properties. However, excessive Ce led to the formation of coarse and brittle phases, causing a decrease in mechanical properties.
The effect of Ce in amount of 0-0.5 wt.% on the microstructure and mechanical properties of the squeeze-cast Al-5Mg-2.2Si-0.6Mn alloys produced by squeeze casting technique was explored. The microstructure was observed by optical microscopy and scanning electron microscopy. The hardness and mechanical properties of the alloys were measured by Vickers hardness and tensile test. The microstructure of the squeeze-cast Al-5Mg-2.2Si0.6Mn alloys is composed mainly of a-Al, Al-Mg2Si eutectic cells, the bulky lath-shaped Al8CeMn4 phase, Al2Mn3 and Al5Mn2Si5 phases after Ce is added. The results show that the addition of Ce leads to the grain refinement, which can improve the mechanical properties. When adding superfluous Ce, the formation of coarse and brittle Al8CeMn4 phase seriously reduces the mechanical properties of the alloy. With the increase of Ce content, the secondary dendrite arm spacing of different alloys decreases first and then increases, hence the hardness and tensile properties increase first and then decrease. The most remarkable improvement in the mechanical properties was acquired in the alloy with 0.10 wt.% Ce addition, the hardness reaches 48.1 HV, the ultimate tensile strength, yield strength and elongation are 265.5 MPa, 185.8 MPa and 5.8%, respectively. (c) 2022 The Author(s). Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).