Design of tough, ductile direct quenched and partitioned advanced high-strength steel with tailored silicon content

Journal

JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T
Volume 17, Issue -, Pages 1390-1407

Publisher

ELSEVIER
DOI: 10.1016/j.jmrt.2022.01.073

Keywords

Direct quenching and partitioning; Dilatometry; Retained austenite; Tempered martensite; Mechanical stability; Toughness

Funding

  1. Academy of Finland [311934]

Ask authors/readers for more resources

The novel processing concept of direct quenching and partitioning (DQ & P) was explored in a medium-carbon steel to evaluate and optimize the processing route for excellent property combinations. Physical simulation studies were conducted to understand the influence of varying silicon contents and processing parameters on microstructural development. The optimized parameters were used to design a processing route for laboratory trials, aiming to produce ultrahigh-strength structural steels with desired mechanical properties.
The novel processing concept of direct quenching and partitioning (DQ & P) has been explored with a medium-carbon (0.4 wt.% C) steel to evaluate and optimize the processing route for excellent property combinations. New compositional design approach was based on physical simulation studies aiming to understand the influence of varying silicon contents (1.5, 0.75 and 0.25 wt.%) and Q & P processing parameters on microstructural development including carbide formation and retained austenite stabilization. Optimized Q & P parameters were selected to design a DQ & P processing route for laboratory hot-rolling trials based on the analyses of physical simulation data. The overall aim of the study was to produce ultrahigh-strength structural steels with yield strength >= 1100 MPa combined with high uniform and total elongation and impact toughness, achieved through designing a low-temperature quenching and partitioning route with effective carbon partitioning. The DQ & P steels gained an excellent combination of mechanical properties comprising of high yield strength of ~1000-1200 MPa and tensile strength-2100-2300 MPa, good elongation (~11-13%), and moderate impact toughness transition temperature T-28J -(-5 to +12 ?). Straining of austenite prior to DQ & P led to an extensive refinement of the final martensitic-austenitic nanostructure. Formation of nanoscale lath-martensite and fine film-like retained austenite structures enabled the observed improvement of mechanical properties. Besides the formation of nano-twinned martensite, inter-lath austenite and transitional carbides were comprehensively characterized. No adverse effect of prolonged partitioning during slow cooling, simulating coiling in actual industrial practice, has been noticed suggesting new possibilities for developing tough, ductile structural steels both for strip/plate products. (C)& nbsp;2022 The Author(s). Published by Elsevier B.V.& nbsp;

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.7
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available