Effect of Dispersing Multiwalled Carbon Nanotubes and Graphene Nanoplatelets Hybrids in the Matrix on the Flexural Fatigue Properties of Carbon/Epoxy Composites

The synergistic effect of applying hybrid nanoparticles in improving the fatigue property of fiber reinforced polymer composites has rarely been explored before. Hence the monotonic and fatigue flexure properties of the carbon fiber reinforced epoxy laminates with matrix modified by multiwalled carbon nanotubes and graphene nanoplatelets were experimentally studied herein. The nanofiller ratio applied in the matrix modification was considered as a variable in the experimental program to investigate the effect of nanofiller ratio on the studied mechanical properties. A synergistic index has been employed to evaluate the synergistic effect of hybrid nanoparticles on the studied properties successfully. Experimental results show that the laminates with matrix modified under a nanofiller ratio (multiwalled carbon nanotube: graphene nanoplatelet) of 9:1 have the higher monotonic and fatigue strengths than those modified under other nanofiller ratios. The monotonic flexural strength and fatigue limit of the specimens modified under a nanofiller ratio of 9:1 are higher than the neat laminate specimens by 9.3 and 11.0%, respectively. The fatigue limits of the studied nano-modified laminates increase with the static strengths. Adding hybrid nanoparticles under proper nanofiller ratios in the matrix can suppress the degradation of the stiffness, further increase the resistance to fatigue damage. Examining the fracture surfaces of fatigued specimens reveals that the pullout/bridging effects of carbon nanotubes and the crack deflection effect of graphene nanoplatelets are the main reinforcement mechanisms in enhancing the fatigue strength of the composites.

Automated summary

The synergistic effect of applying hybrid nanoparticles in improving the fatigue property of fiber reinforced polymer composites is studied in this paper. The experimental results show that fiber reinforced polymer composites modified with hybrid nanoparticles under proper nanofiller ratios have higher fatigue strengths. The observation of fracture surfaces reveals that the pullout/bridging effects of carbon nanotubes and the crack deflection effect of graphene nanoplatelets are the main reinforcement mechanisms in enhancing the fatigue strength of the composites.