hybrid joint; thermoplastic; thermoset; titanium; spot-welding; carbon fiber; electron beam
Categories
Funding
- Japan Society for the Promotion of Science (JSPS)
Ask authors/readers for more resources
This article provides a literature review of the latest methods to strengthen Ti/carbon-fiber-reinforced polymer (CFRP) hybrid joints. It suggests the use of carbon fiber plug insert to enhance the safety levels of aircraft fan blades. The study also explores a novel method involving low voltage electron beam irradiation (HLEBI) to activate carbon fibers and improve the joint strength.
A literature review of up-to-date methods to strengthen Ti/carbon-fiber-reinforced polymer (CFRP) hybrid joints is given. However, there are little or no studies on Ti/CFRP joints by carbon fiber plug insert, which takes advantage of the extremely high surface adhesion area of similar to 6 mu m CFs. Therefore, we cover the current status and review our previously published results developing hybrid joints by a CF plug insert with spot-welded Ti half-lengths to enhance the safety levels of aircraft fan blades. A thermoset Ti/CF/epoxy joint exhibited an ultimate tensile strength (UTS) of 283 MPa when calculated according to the rule of mixtures (RM) for the CF cross-section portion. With concern for the environment, thermoplastic polymers (TPs) allowed recyclability. However, a drawback is easy CF pull-out from difficult-to-adhere TPs due to insufficient contact sites. Therefore, research on a novel method of homogeneous low voltage electron beam irradiation (HLEBI) to activate a bare CF half-length prior to dipping in a TP resin was reviewed and showed that the UTS by the RM of Ti/EBCF/acrylonitrile butadiene styrene (ABS) and Ti/EBCF/polycarbonate (PC) joints increased 154% (from 55 to 140 MPa) and 829% (from 30 to 195 MPa), respectively, over the untreated sample. The optimum 0.30 MGy HLEBI prevented CF pull-out by apparently growing crystallites into the TP around the CF circumference, raising the UTS amount closer to that of epoxy.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available