Ceramics; Aluminosilicates; Sorbents; Cesium; Radionuclides, Leaching Rate; Hydrolytic stability; Sintering; SPS
Categories
Funding
- State Assignment of the Ministry of Science and Higher Education of the Russian Federation [00657-2020-0006]
- Strategic Priority Research Program of the Chinese Academy of Sciences [XDA22010301]
Ask authors/readers for more resources
Hydrothermal synthesis of NaY-type zeolite was conducted to investigate the effect of temperature on its properties. Solid-state matrices based on NaY zeolite were obtained through spark plasma sintering, which showed high values of compressive strength and hardness. The physical and chemical stability of the ceramic matrix was studied using various analytical methods.
Hydrothermal synthesis of NaY-type zeolite was carried out and the effect of temperature on the phase composition, crystal structure, textural characteristics, particle size and morphology, as well as sorption properties to Cs+ ions was studied. Solid-state matrices based on NaY zeolite the Faujasite structure containing 26.1 wt% cesium were obtained by spark plasma sintering (SPS) with high values of compressive strength (to 132.9 MPa) and Vickers microhardness to HV similar to 698, Fracture toughness (K-1c) similar to 1.26 MPa m(1/2). The kinetics of ceramic matrices consolidation, phase composition and morphology using dilatometric studies, XRD, and SEM were studied. The thermogravimetric analysis shown the high thermal stability of the obtained samples up to 1300 degrees C. The high hydrolytic stability of CsAlSiO4 ceramic was proven (leaching rate of 2.33 x 10(-8) g.cm(-2).day(-1) and cesium diffusion coefficient De 1.41 x10(-13)), which exceeds the requirements of GOST R 50926-96 and ISO 6961:1982 for solid-state matrices.