JOURNAL OF ALLOYS AND COMPOUNDS
Volume 688, Issue -, Pages 130-139Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2016.07.103
Keywords
Tin sulphides; Thin films; Laser treatment; Phase transition; Phase composition
Categories
Funding
- Ministry of Education and Science of Ukraine [0115U000665c]
Ask authors/readers for more resources
thin film of SnS2 obtained by close-spaced vacuum sublimation was irradiated by an Nd:YAG laser (lambda = 532 nm) using two intensities of laser radiation of 8.5 MW/cm(2) and 11.5 MW/cm(2). It was shown that laser irradiation leads to evaporation of sulphur from the surface, and the formation of SnS and Sn2S3 phases. The study of samples' cross-section by energy dispersive X-ray analysis reveals that in the case of irradiation at 8.5 MW/cm(2) intensity, the SnS layer is formed only at the surface of the initial SnS2 thin film. The application of more intensive radiation of 11.5 MW/cm(2) leads to changes in chemical composition for the entire thin film. The formation of the predominant SnS phase, which includes a small amount of Sn2S3, was confirmed by the X-ray diffraction and Raman spectroscopy methods, as well as by measurements of optical reflectance and transmittance spectra. It was established that laser irradiation of the samples leads to the coalescence of grains accompanied by smoothing of the surface. The current-voltage characteristics of the ITO/SnxSy/Al samples show an ohmic behaviour in the case of non-irradiated intensity samples; for irradiated samples, the diode behaviour of I-V curves was observed. This is considered as evidence of the formation of p-SnS/n-SnS2 heterojunction by laser irradiation. (C) 2016 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available