High performance langasite based SAW NO2 gas sensor using 2D g-C3N4@TiO2 hybrid nanocomposite

Nitrogen dioxide (NO2) gas has emerged as a severe air pollutant that causes damages to the environment, human life and global ecosystems etc. However, the currently available NO2 gas sensors suffers from insufficient selectivity, sensitivity and long response times that impeding their practical applicability for room temperature (RT) gas sensing. Herein, we report a high performance langasite (LGS) based surface acoustic wave (SAW) RT NO2 gas sensor using 2-dimensional (2D) g-C3N4@TiO2 nanoplates (NP) with {001} facets hybrid nanocomposite as a chemical interface. The g-C3N4@TiO2 NP/LGS SAW device showed a significant negative frequency shift (Delta f) of similar to 19.8 kHz which is 2.4 fold higher than that of the pristine TiO2 NP/LGS SAW sensor toward 100 ppm of NO2 at RT. In addition, the hybrid SAW device fascinatingly exhibited a fast response/recovery time with a low detection limit, high selectivity, and an effective long term stability toward NO2 gas. It also exhibited an enhanced and robust negative frequency shifts under various relative humidity conditions ranging from 20% to 80% for 100 ppm of NO2 gas. The high performance of the g-C3N4 @TiO2 NP/LGS SAW gas sensor can be attributed to the enhanced mass loading effect which was assisted by the large surface area, oxygen vacancies, OH and amine functional groups of the n-n hybrid heterojunction of g-C3N4@TiO2 NP that provide abundant active sites for the adsorption and diffusion of NO2 gas molecules. These results emphasize the significance of the integration of 2D materials with metal oxides for SAW based RT gas sensing technology holds great promise in environmental protection.

Automated summary

In this study, a high-performance langasite-based surface acoustic wave (SAW) gas sensor for nitrogen dioxide (NO2) at room temperature was developed. The sensor exhibited excellent selectivity, sensitivity, and response time, as well as stability in various relative humidity conditions. The integration of 2D materials with metal oxides shows promise for environmental protection.