Chemical disorder in polycrystalline Ni2MnGa thin films

The chemical disorder in magnetic shape memory alloys it is an important parameter that impacts on its magneto-mechanical and electronic properties. In this work, Ni2MnGa thin films were deposited on flexible glass substrates by using DC magnetron sputtering technique. The short-range order/disorder was in-vestigated by means of Extended X-ray absorption fine structure (EXAFS) and X-ray absorption near-edge structure (XANES) measurements using at Mn K-edge. Polycrystalline samples of Ni2MnGa with fixed stoichiometry exhibit L2(1) structure with low residual stress and similar grain sizes. A phenomenological model taking into account three chemical order parameters associated with main chemical anti-site disorders and reliable lattice tetragonal distortions extracted from X-ray diffraction analyses was used to perform systematic computational simulations. The results reveal the persistence of local tetragonal distortions of the crystal structure with L21 structure under when increasing annealing temperatures that are accompanied by a systematic decrease of the anti-site disorder between Ni and Mn atoms and substitutions between Ni and Ga atoms, with the orderly occupation of the atomic sites of Mn and Ga remaining unstable. This work also shows presents a consistent model to perform quantitative analyses of the chemical anti-site disorders through EXAFS measurements in the on Ni2MnGa polycrystalline thin films that preserve both the stoichiometry and the L2(1) crystalline structure. (C) 2021 Elsevier B.V. All rights reserved.

Automated summary

The chemical disorder in magnetic shape memory alloys has a significant impact on their properties. This study deposited Ni2MnGa thin films on flexible glass substrates using DC magnetron sputtering and investigated the short-range order/disorder through X-ray absorption measurements. The results reveal the persistence of local tetragonal distortions, decrease of anti-site disorder, and substitutions between Ni and Ga atoms with increasing annealing temperatures.