Iron ore pellet; Swelling; Silica; Basicity; Microstructure; Physical and metallurgical properties
Categories
Ask authors/readers for more resources
At JSW Steel Limited (JSWSL), pellets form the major part of the iron-bearing feed to corex and blast furnace. JSWSL produces low-basicity pellets ((CaO/SiO2) - 0.40 to 0.50). The quality of the pellet is affected by the raw material chemistry (gangue content), flux proportion and their subsequent heat treatment to produce the fired pellets. The raw material silica, limestone addition, i.e. basicity - CaO/SiO2 of pellet decides the mode, temperature and the amount of melt formed. The properties of the pellets are, therefore, largely governed by the form and degree of bonding achieved between ore particles and also by the stability of these bonding phases during the reduction of iron oxides. In the present study, laboratory pelletisation experiments have been carried out to know the effects of silica and basicity on the microstructure and swelling behaviour of pellets during reduction. Phase analysis was carried out using image analyser, and chemical analysis of oxide and slag phases was carried out using SEM-EDS. From the laboratory studies, it was observed that the swelling index of the pellets decreased with an increase in silica content due to the decrease in porosity. The presence of higher silica in pellet hinders the reduction step of haematite to magnetite at lower temperatures. Pellets with basicity range 0 to 0.1 exhibited lower swelling index due to the formation of high melting point fayalite phase and also at this basicity range the structure is held together by the seam-like compounds between Fe2O3 and SiO2 primarily at high silica content. Higher swelling index was observed at the basicity range 0.3 to 0.7 due to the presence of low melting point calcium olivines (1115 degrees C) between fayalite (FeSiO4) and dicalcium silicate (Ca2SiO4). Low melting point slag phase enhances the swelling index of the pellets. Swelling index of the pellets considerably dropped between the basicity range 0.9 to 1.1 due to the formation of calcium ferrite phases with a close pore structure.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available