Keywords
all-solid-state devices; chlorine-doped graphene; electrochemical exfoliation; high volumetric energy density; micro-supercapacitors
Categories
Funding
- National Natural Science Foundation of China [51772133]
- Shandong Province [ZR2017JL022]
- project of 20 items of University of Jinan [2018GXRC001]
- Case-by-Case Project for Top Outstanding Talents of Jinan
- China Scholarship Council [202008370267]
- MOE Singapore [MOE2018-T2-2-095]
Ask authors/readers for more resources
Graphene-constructed micro-supercapacitors have gained attention due to their tunable power output, mechanical flexibility, and long cyclability. In this study, high-quality chlorine-doped graphene nanosheets were fabricated using an eco-friendly electrochemical exfoliation process. The resulting all-solid-state micro-supercapacitor exhibited a large reversible capacity, steady charge/discharge performance, and high volumetric capacitance and energy density.
Graphene-constructed micro-supercapacitors (MSCs) have received considerable attention recently, as part of the prospective wearable and portable electronics, owing to their distinctive merits of well-tunable power output, robust mechanical flexibility, and long cyclability. In the current work, the focus is on the fabrication of high-quality and solution-processible chlorine-doped graphene (Cl-G) nanosheets through a handy yet eco-friendly electrochemical exfoliation process. The Cl-G is characteristic of the large lateral size of approximate to 10 mu m, abundant nanopores with sizes of as small as 2 nm, as well as numerous steps from the rugged surface. Arising from the rich chemical functionalities and structure defects, the all-solid-state MSC built by using Cl-G via a facile mask-assisted method delivers a large reversible capacity and ultrasteady charge/discharge performance, with the capacitance being maintained at 98.1% even after 250 000 cycles. The Cl-G-MSC with EMIMBF4/PVDF-HFP as the electrolyte displays a large volumetric capacitance up to 160 F cm(-3) at the scan rate of 5 mV s(-1) and high volumetric energy density of 97.9 mW h cm(-3) at the power density of 3.4 W cm(-3). The device can also output a high voltage up to 3.5 V and robust capability with 94.8% of capacitance retention upon 10 000 cycles.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available