Journal
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
Volume 41, Issue 34, Pages 15124-15132Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.ijhydene.2016.06.248
Keywords
PEM water electrolysis; Supported anode catalyst; Iridium; Thin film; Titanium carbide
Categories
Funding
- CERIC Consortium
- Czech Ministry of Education [INGO LG15050]
- Grant Agency of the Charles University in Prague (GAUK) [236214]
Ask authors/readers for more resources
Proton exchange membrane (PEM) water electrolysis (PEMWE) is getting more attention in recent years as a promising alternative in context of energy storage from renewables. However high prices of platinum and iridium, currently considered to be the state-of-the-art electrocatalysts, prevent wider commercialization of this technology. In this paper, we present unconventional and cost-effective preparation method of anode catalyst, containing low amount of noble metal. Thin Ir film is magnetron sputtered on TiC-based support sublayer, hot-pressed on anode side of Nafione (R) N115 PEM. Following three parameters were systematically varied and their impact on PEMWE in-cell performance was evaluated: total TiC-based support material loading on the PEM, ionomer content within the support sublayer and Ir catalyst loading on top of the support sublayer. In addition, TiC-based sublayer underwent accelerated aging procedure, followed by photoelectron spectral analysis to prove its ability to withstand high anodic potentials. Remarkable PEMWE in-cell performances were obtained, considering amount of used Ir; 1.74 V (with similar to 80 mu g cm(-2) of Ir), 1.72 V (with similar to 160 mu g cm(-2) of Ir) and 1.71 V (with similar to 240 mu g cm(-2) of Ir) at 1 A cm(-2) and 80 degrees C. (C) 2016 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available