Long-Term Degradation of Passivated Emitter and Rear Contact Silicon Solar Cell under Light and Heat

Advanced designs enable high-efficiency solar cells; however, more complex structures create new long-term stability concerns. Herein, the long-term degradation processes affecting advanced silicon solar cells using laboratory-based illumination and heating over hundreds of hours are investigated. The activation energy for the degradation of voltage is estimated and the degradation rates to normal solar cell operating temperature ranges are extrapolated. The cell degradation observed at high temperatures in the lab is kinetically similar to the process affecting field-deployed modules contributing to 0.37% year(-1) of annualized degradation. Electroluminescence and photoluminescence mapping show that the degradation is dominated by minority carrier lifetime reduction. Suns-open-circuit voltage and light beam-induced current results indicate that the degradation could result from passivation degradation at the surface or defect formation in the near-subsurface region, leading to increased minority carrier recombination. This work highlights a long-term degradation process under elevated temperature and illumination that may continue to affect cells in an irreversible manner that is separate from recoverable light-induced degradation and light- and elevated temperature-induced degradation.

Automated summary

The study investigates the long-term degradation processes affecting advanced silicon solar cells under laboratory-based illumination and heating, with findings showing that the degradation is mainly attributed to reduction in minority carrier lifetime. Furthermore, it is highlighted that degradation under elevated temperature and illumination conditions may continue to affect cells in an irreversible manner.