Recent Progress on Sulfated Nanozirconia as a Solid Acid Catalyst in the Hydrocracking Reaction

Zirconia has advantageous thermal stability and acid-base properties. The acidity character of ZrO2 can be enhanced through the sulfation process forming sulfated zirconia (ZrO2-SO4). An acidity test of the catalyst produced proved that the sulfate loading succeeded in increasing the acidity of ZrO2 as confirmed by the presence of characteristic absorptions of the sulfate group from the FTIR spectra of the catalyst. The ZrO2-SO4 catalyst can be further modified with transition metals, such as Platinum (Pt), Chromium (Cr), and Nickel (Ni) to increase catalytic activity and catalyst stability. It was observed that variations in the concentrations of Pt, Cr, and Ni produced a strong influence on the catalytic activity as the acidity and porosity of the catalyst increased with their addition. The activity, selectivity, and catalytic stability tests of Pt/ZrO2-SO4, Cr/ZrO2-SO4 and Ni/ZrO2-SO4 were carried out with their application in the hydrocracking reaction to produce liquid fuel. The percentage of liquid fractions produced using these catalysts were higher than the fraction produced using pure ZrO2 and ZrO2-SO4 catalyst.

Automated summary

Zirconia with enhanced acidity through sulfation process can be modified with transition metals to improve catalytic activity and stability. The catalytic tests showed that the modified catalysts had higher activity and produced more liquid fuel compared to pure ZrO2 and ZrO2-SO4 catalyst.