Journal
INTERNATIONAL JOURNAL OF BIOLOGICAL MACROMOLECULES
Volume 86, Issue -, Pages 606-612Publisher
ELSEVIER SCIENCE BV
DOI: 10.1016/j.ijbiomac.2016.01.104
Keywords
Tara gum; Cellulose nanocrystals; Nanocomposite films; Physical properties
Funding
- National Natural Science Foundation of China [31470612]
Ask authors/readers for more resources
Cellulose nanocrystals (CNC) prepared from microcrystalline cellulose were blended in tara gum solution to prepare nanocomposite films. The morphology, crystallinity, and thermal properties of the CNC and films were evaluated by using transmission electron microscopy, X-ray diffractometry, and thermogravimetric analysis, respectively. The resultant CNC was rod-shaped with diameters of around 8.6 nm. The effect of CNC content on physical and thermal properties of films was studied. The composite film tensile strength increased from 27.86 to 65.73 MPa, elastic modulus increased from 160.98 MPa to 882.49 MPa and the contact angle increased from 55.8 degrees to 98.7 degrees with increasing CNC content from 0 to 6 wt%. However, CNC addition increased the thermal stability slightly and CNC content above 6 wt% decreased the tensile strength by CNC aggregation in the matrix. The nanocomposite film containing 6 wt% CNC possessed the highest light transmittance, mechanical properties, and lowest oxygen permeability. CNC addition is a suitable method to modify tara gum matrix polymer properties. (C) 2016 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available