AimTo evaluate the effect of 17% ethylenediaminetetraacetic acid (EDTA), 2.25% peracetic acid (PA) or 10% citric acid (CA) on the push-out bond strength of calcium silicate-based endodontic sealers [MTA Fillapex (Angelus, Londrina, Brazil) and Total Fill BC Sealer (FKG, La Chaux-de-Fonds, Switzerland)] to root dentine after different periods of immersion in phosphate-buffered saline (PBS). AH Plus (Dentsply DeTrey, Konstaz, Germany) was used as a reference material for comparison. MethodologyThirty human maxillary incisors were selected and three 1-mm discs were obtained from the middle third of each root. On the axial surface of each disc, three 0.8-mm-diameter holes were drilled through the dentine. After standardized irrigation, each dentine disc from the same root was treated for smear-layer removal with one of the three tested chelating solutions: EDTA, PA or CA. After that, the holes were dried with paper points and filled with one of the three test root canal sealers. The filled dental slices were further immersed in PBS solution (pH 7.2) for 7days (T1) or 30days (T2) at 37 degrees C, before the push-out assay. Friedman, Kruskal-Wallis and Mann-Whitney tests were used respectively to estimate the impact of the independent variables (solutions, sealers and period of PBS immersion) on the push-out bond strength. The level for significance was set at =5% and data were further subjected to a Bonferroni correction. ResultsSolutions and periods of immersion did not significantly influence the displacement resistance (P=0.285, and P=0.104, respectively) of sealers to root dentine. On the other hand, the type of sealer significantly affected the push-out bond strength (P=0.000). AH Plus was associated with greater resistance to dislodgment compared with Total Fill BC Sealer and MTA Fillapex (P=0.000). MTA Fillapex resulted in the lowest push-out bond strength (P=0.000). ConclusionThe use of different chelating agents did not influence the push-out bond strength of endodontic sealers. Calcium silicate-based sealers had lower push-out bond strength values compared with a conventional epoxy resin-based sealer (AH Plus).
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available