A novel nitrogen-rich phosphinic amide towards flame-retardant, smoke suppression and mechanically strengthened epoxy resins

In this work, aiming to obtain multifunctional epoxy resin (EP) possessing flame retardancy and light smoke without compromising the mechanical properties, a novel nitrogen-rich phosphinic amide named D-5-AT was synthesized and then incorporated to EP. The results showed that UL-94 V-0 rating of EP with 7.5 wt% D-5-AT was available and limiting oxygen index (LOI) was up to 35.1%. Meanwhile, in the presence of D-5-AT, the heat release and smoke production of EP/D-5-AT materials were effectively suppressed during combustion as compared with EP. The improvement mentioned above was found related to the condensed and gaseous flame retardant effect of D-5-AT through the investigation on char residues of EP/D-5-AT materials and volatiles of D-5-AT. Besides, because of the existence of more hydrogen bonds and bulky group by virtue of the introduction of D-5-AT, the mechanical properties of modified EP were strengthened as well. This work offered a promising method to meet the ever-increasing requirement of multi-functionality of epoxy resins. (C) 2022 Elsevier Ltd. All rights reserved.

Automated summary

In this study, a nitrogen-rich phosphinic amide named D-5-AT was synthesized and incorporated into epoxy resin (EP) to achieve multifunctionality without compromising mechanical properties. The addition of D-5-AT significantly improved the flame retardancy and smoke suppression of EP, while also strengthening its mechanical properties. This work offers a promising method to meet the increasing demand for multifunctional epoxy resins.