Journal
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
Volume 543, Issue -, Pages -Publisher
ELSEVIER
DOI: 10.1016/j.jmmm.2021.168624
Keywords
Double perovskites; New compositions; Powder X-ray diffraction; Magnetic properties
Funding
- Institute of Solid State Chemistry of the Ural Branch of the Russian Academy of Sciences [A19-119031890025-9]
- RFBR [19-03-00671]
Ask authors/readers for more resources
Solid solutions based on Sr2MnSbO6 and SrLaMnSbO6 with mixed oxidation states of Mn were prepared by solid state synthesis. The structural and magnetic properties of these solid solutions were studied, revealing that the dominant exchange interactions between Mn3+ and Mn2+ cations in Sr2-xLaxMnSbO6 are of antiferromagnetic nature.
Solid solutions (SS) based on Sr2MnSbO6 and SrLaMnSbO6 with mixed oxidation states of Mn have been prepared by solid state synthesis under standard conditions. The structural and magnetic properties of Sr2-xLaxMnSbO6 and Sr1.5La0.5Mn1+ySb1-yO6 have been studied using X-ray diffraction data and magnetic susceptibility chi and magnetization sigma measurements at 2-400 K. The samples of the first group crystallize in the monoclinic space group P21/n, their unit cell volume increases with x due to the formation of mixed Mn3+/Mn2+ valence. The change of the Weiss constant Theta sign from positive to negative with variation of x, as well as the divergence between FC and ZFC dependences chi(T) below 40 K and spin-glass behavior indicate that the dominant exchange interactions between Mn3+ and Mn2+ cations in Sr2-xLaxMnSbO6 are of antiferromagnetic nature. The samples of the second group (at y = 0.25 and 0.50) were characterized as non-uniform, containing apparently two phases with a mixed Mn3+/Mn4+ state. The composition of the phases was established approximately by studying their structural and magnetic characteristics. The composition and crystal structure of the main phases are similar to those of the monoclinic samples described above. The secondary phases are identified as rhombohedral (space group R3c) with ferromagnetic properties with TC of 304.2 K (y = 0.25) and 365 K (y = 0.50).