Adsorption and photocatalytic properties of porphyrin loaded MIL-101 (Cr) in methylene blue degradation

In this study for the very first time, zinc tetraphenylporphyrin (ZnTPP) was loaded into MIL-101 (Zn[TPP]@MIL-101) to perform an adsorptive and photocatalytic dye removal. The physicochemical attributes of the catalyst were thoroughly determined by the usage of XRD, FTIR, FESEM, BET, UV-vis, and inductively coupled plasma (ICP). The obtained XRD pattern exhibited the phase purity of MIL-101 and its structural stability. The solid-phase diameter of the catalyst was observed to be similar to 270.76 +/- 119.95 nm, while its gas adsorption data was indicative of a decrease in the specific surface area after the loading of ZnTPP. The ICP analysis displayed the amount of encapsulated Zn[TPP] (similar to 17%) in MIL-101. The UV-vis confirmed the presence of Zn[TPP] in MIL-101 with the lack of any interferences or overlaps with the lambda(max) of methylene blue (MB) with the support. The dye removal of MB was investigated under dark conditions (adsorption) and UV light (photodegradation). The observed adsorption under dark conditions using Zn[TPP]@MIL-101 (99.27% yield) demonstrated a superior dye removal in comparison to the cases of photodegradation of MB by MIL-101 and Zn[TPP] @ MIL-101 or adsorption by MIL-101. In conformity to the gathered results, [ZnTPP] was able to increase the adsorption capacity at pH =7 at room temperature.

Automated summary

In this study, zinc tetraphenylporphyrin was loaded into MIL-101 to remove dyes through adsorption and photocatalysis. The physicochemical properties of the catalyst were thoroughly characterized. The results showed that Zn[TPP]@MIL-101 exhibited superior dye removal under dark conditions.