Damage formation mechanisms of sintered silicon carbide during single-diamond grinding

Journal

CERAMICS INTERNATIONAL
Volume 47, Issue 20, Pages 28419-28428

Publisher

ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2021.06.259

Keywords

Microstructure; Damage formation; Grain boundary; Dislocation pileup; Crack initiation; Surface; subsurface morphology

Funding

  1. China Postdoctoral Science Foundation [2020M681761]
  2. Fundamental Research Funds for the Central Universities [2021-11038]

Ask authors/readers for more resources

By conducting a single-diamond grinding test on SSiC, researchers were able to identify stages of purely ductile, primarily ductile, primarily brittle, and purely brittle behavior during the grinding process. The high density of dislocations and amorphization of SiC grains were found to be responsible for the plastic deformation of SSiC, with stress concentration at grain boundaries being the main mechanism for crack initiation.
In this research, a single-diamond grinding test was performed on sintered silicon carbide (SSiC) to explore the damage formation mechanism. A scanning electron microscope and a transmission electron microscope (TEM) were used to examine the surface and subsurface morphologies of the grinding groove, respectively. The characteristics of the ground surface morphologies reveal that the single-diamond grinding process of SSiC can be classified into purely ductile, primarily ductile, primarily brittle, and purely brittle stages. Based on the highresolution TEM (HRTEM) images and the corresponding Fast Fourier transform images of the near-surface region, results reveal that the high density of dislocations and amorphization of SiC grains are responsible for the plastic deformation of SSiC. Most of the cracks congregate on the top grains of the ground surface due to the distinct obstruction of the grain boundary on the cracks propagation, and the cracks generated at the grain boundaries emit into the top grain interiors and go up toward the exposed surface for the distortedly deformed region with higher strain energy; Furthermore, stress concentration caused by the dislocation pileups at grain boundaries represents the crack initiation mechanisms for SSiC. Finally, based on the dislocations pile-up theory, a critical undeformed chip thickness model for boundary crack system nucleation is established, which considers the cutting-edge radius, grinding wheel speed, material properties, and grain size of ceramics.

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.7
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available