One-Step Synthesis of Degradable Vinylic Polymer-Based Latexes via Aqueous Radical Emulsion Polymerization

Aqueous emulsion copolymerizations of dibenzo[c,e]oxepane-5-thione (DOT) were performed with n-butyl acrylate (BA), styrene (S) and a combination of both. In all cases, stable latexes were obtained in less than two hours under conventional conditions; that is in the presence of sodium dodecyl sulfate (SDS) used as surfactant and potassium persulfate (KPS) as initiator. A limited solubility of DOT in BA was observed compared to S, yielding to a more homogeneous integration of DOT units in the PS latex. In both cases, the copolymer could be easily degraded under basic conditions. Emulsion terpolymerization between DOT, BA and S allowed us to produce stable latexes not only composed of degradable chains but also featuring a broad range of glass transition temperatures.

Automated summary

Aqueous emulsion copolymerizations of dibenzo[c,e]oxepane-5-thione (DOT) with n-butyl acrylate (BA), styrene (S) and a combination of both were successfully performed. DOT showed limited solubility in BA compared to S, resulting in a more homogeneous integration of DOT units in the latex. Emulsion terpolymerization also produced stable latexes with a broad range of glass transition temperatures.