Dynamic Weld evolution during ultrasonic welding of Cu-Al joints

Publisher

ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2021.141724

Keywords

Ultrasonic welding; Copper; Aluminum; Molecular dynamics simulation; EBSD

Funding

  1. National Natural Science Foundation of China [NSFC 51775140]
  2. National Science and Technology Major Project [2017VI00090080]
  3. Guangdong Province key research and development program [2019B010935001]
  4. Shenzhen Science and Technology Plan [JCYJ20180507183511908, 20200821172456002]
  5. Bureau of Industry and Information Technology of Shenzhen through the innovation chain and industry chain [201806071354163490]

Ask authors/readers for more resources

This study comprehensively investigated dissimilar welds of aluminum alloy 1060 to T2 copper, finding that microwelds first formed at high asperities, followed by severe plastic deformation and attachment. With increasing welding time, the lap shear failure loads for the joints gradually increased and reached maximum values. The microstructural evolution of the joint mainly focused on the softer material side, providing new insights into ultrasonic welding of dissimilar metals.
Although ultrasonic welding of dissimilar metals has been widely applied in the automotive and electronic industries, the dynamic weld evolution, including deformation, breakage, and attachment, is still in a conjecture stage because of the short welding time, thin reaction layer and complex thermomechanical behavior. In this study, dissimilar welds of aluminum (Al) alloy 1060 to T2 copper (Cu) were comprehensively investigated via microstructural characterization, molecular dynamics simulations, and mechanical tests. It was found that microwelds first formed at high asperities. Subsequently, the continuous relative friction at the interface induced severe plastic deformation on the Al side, resulting in the alternating fracture and formation of micro-welds, flattening of asperities, and attachment of Al on the Cu surface. The lap shear failure loads for the joints gradually increased with increasing welding time. The failure loads reached the maximum values of 0.9 +/- 0.03 kN after a welding time of 0.29 s. Furthermore, the Cu asperities completely sunk into the Al matrix, presenting a macro-interlocking morphology at the interface. A swirl-like grain morphology with no deformation texture appeared simultaneously on the Al side. Analysis of the weld formation indicated that microstructural evolution of the joint, including material flow, grain morphology, and grain orientation, was mainly concentrated on the softer material side, providing a new understanding of the ultrasonic welding of dissimilar metals.

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.7
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available