Sol-Gel coated WO3 thin films based complementary electrochromic smart windows

The WO3 films were prepared via sol-gel dip coating method. The optical, structural, morphological, electrochemical and electrochromic properties of the prepared films were studied. The WO3 film coated on glass substrate exhibits 74% transmission at 550 nm. XRD studies indicate the WO3 films in the amorphous state. FTIR spectrum confirms the formation of WO3. The FESEM image confirms the formation of smooth surface. The cyclic voltammetric study reveals the anodic/cathodic diffusion coefficients of 2.31/4.79 x 10-12 cm2/s for WO3 films. The film thickness was about 260 nm. The same film shows a change in optical transmission of 55.37% at 550 nm. The sol-gel coated WO3 films were used to develop the complementary electrochromic smart windows in conjugation with NiO and Ni0.95Co0.05O as an anode. A five layered EC windows were developed and studied with Li' and H' conducting gel electrolytes. (c) 2021 Elsevier B.V. All rights reserved.

Automated summary

WO3 films were prepared via sol-gel dip coating method and their properties were studied. The films exhibited 74% transmission on glass substrate, with a thickness of about 260 nm and a smooth surface. They were used to develop complementary electrochromic smart windows in conjunction with NiO and Ni0.95Co0.05O.