A novel degradable tricalcium silicate/calcium polyphosphate/polyvinyl alcohol organic-inorganic composite cement for bone filling

In this study, tricalcium silicate (C3S) calcium/polyphosphate/polyvinyl alcohol organic-inorganic self-setting composites were successfully designed. A variety of tests were conducted to characterize their self-setting properties, mechanical properties, degradation properties, and related biological properties. The composite bone cements showed a short setting time (5.5-37.5 min) with a 5:5-6:4 ratio of C3S/CPP to maintain a stable compressive strength (28 MPa). In addition, PVA effectively reduced the brittleness of the inorganic phase. Degradation experiments confirmed the sustainable surface degradation of bone cement. A maximum degradation rate of 49% was reached within 56 days, and the structure remained intact without collapse. Culturing MC3T3 cells with bone cement extracts revealed that the composite bone cements had excellent biological properties in vitro. The original extract showed a proliferation promotion effect on cells, whereas most of the other original extracts of degradable bone cements were toxic to the cells. Meanwhile, extracellular matrix mineralization and alkaline phosphatase expression showed remarkable effects on cell differentiation. In addition, a good level of adhesion of cells to the surfaces of materials was observed. Taken together, these results indicate that C3S/CPP/PVA composite bone cements have great potential in bone defect filling for fast curing.

Automated summary

The study successfully designed a C3S/CPP/PVA composite bone cement with self-setting and excellent biological properties, which has great potential in bone defect filling. Through various tests and experiments, the potential of the composite bone cement was confirmed.