Journal
JOURNAL OF ALLOYS AND COMPOUNDS
Volume 874, Issue -, Pages -Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2021.159861
Keywords
Complex dopant; Aluminium; Fluorine; Dielectric properties
Categories
Funding
- Research program of the Ukrainian National Academy of Sciences New functional substances and materials for chemical production (Fine Chemicals) [0119U101351]
Ask authors/readers for more resources
The resistances of grain boundary and interface between sample and electrode increase with the combined introduction of Al3+ and F- ions. After 12 hours of sintering, a decrease in dielectric properties was observed due to copper losses. Samples sintered for 10 hours at 1 kHz exhibit specific dielectric parameters.
The ceramics CaCu3Ti4-xAlxO12-0.5x-yFy were prepared using solid-state reactions technique and pre-synthesized CaTiO3. It was found that the resistances of both the grain boundary RGB and the interface between sample and electrode RSE increase at the combined introduction of Al3+ and F- ions. At 1100 degrees C, a decrease in dielectric properties after 12 h of sintering time due to copper losses was observed. The samples with x/ y = 0.04/0.04 sintered for 10 h at 1 kHz are characterized by the following dielectric parameters: epsilon' approximate to 72,000 and tan delta approximate to 0.047. In the sample x/y = 0.04/0, the lowest dielectric loss (tan delta approximate to 0.044) were found. (c) 2021 Elsevier B.V. All rights reserved.