Enhanced cycling performance of binder free silicon-based anode by application of electrochemically formed microporous substrate

In this work, an electrochemically formed porous Cu current collector (p-Cu) is utilized for the development of a high-performance binder-free silicon anode. Two electrolyte compositions based on sulfolane (SL) and [BMP][TFSI] ionic liquid (IL) are implemented for silicon deposition. The electrochemical experiments confirm the advantages of applying the p-Cu structure in terms of specific capacity, rate capability, and long-term cycling, where the best electrochemical properties have been observed for the Si deposited from SL electrolyte. The Si-based p-Cu anodes formed in SL display stable 2500 mAh g(-1) reversible capacity during the first 250 cycles and promising capacity retention. Compared to this result, the cycling performance of the same type of material deposited on flat Cu foil (f-Cu) showed significantly reduced capacity (1400 mAh g-1) and inferior cycling performance. The positive effect can be attributed to the improved mechanical stability of the active material and accelerated ionic transport in the porous structure of the anode. The improved functional properties of the electrochemically deposited Si from SL electrolyte in p-Cu samples compared to those obtained in IL can be ascribed to differences in the chemical composition. While the layers deposited in SL electrolyte involve Si domains incorporated in a matrix containing C and O that offer high mechanical stability, the Si material obtained in IL is additionally influenced by N and F chemical species, resulting from active IL decomposition. These differences in the chemical surrounding of the Si domains are the primary reason for the inferior electrochemical performance of the material deposited from [BMP][TFSI] electrolyte. XPS analysis shows that the initial composition of the as deposited layers, containing a considerable amount of elemental Si, is changed after lithiation and that the electrochemical activity of the anode is governed by switching between the intermediate redox states of Si, where the carbon-oxygen matrix is also involved. (C) 2021 Elsevier Ltd. All rights reserved.

Automated summary

The study utilized a porous Cu current collector for a high-performance binder-free silicon anode, showing superior electrochemical performance for Si deposited from SL electrolyte compared to IL electrolyte. Differences in chemical composition were identified as the primary reason for the improved functional properties in the former.