Dentin anti-demineralization potential of surface reaction-type pre-reacted glass-ionomer filler containing self-adhesive resin cement

Objective To investigate the anti-demineralization potential of a newly developed surface reaction-type pre-reacted glass-ionomer (S-PRG) filler containing self-adhesive resin cement against acidic attacks on the dentin surface. Materials and methods A total of 32 bovine teeth were used. Cavities were prepared on crown dentin slaps and filled with three self-adhesive resin cement: (1) S-PRG-based cement, (2) Si-based cement, and (3) RelyX cement. Specimens were then subjected to pH cycling for 28 days, and the depth of demineralization was assessed using swept-source optical coherence tomography (SS-OCT) after 7, 14, 21, and 28 days. Sixty-four root dentin blocks were divided into four groups and then subjected to a pH cycling procedure with the aforementioned three material blocks and one negative control. The mineral loss was observed using transverse microradiography (TMR), and the surface microhardness (SMH) test was conducted to investigate the mechanical properties of treated dentin surfaces. Results The depth of demineralization for the S-PRG-based cement was significantly lower than that of the Si-based cement after 7, 21, and 28 days. Conversely, the RelyX cement was not significantly different from the Si-based cement after 7, 14, and 21 days (p < 0.05). Regarding the TMR and SMH test, the S-PRG-based cement showed the least mineral loss with the highest resistance to acidic challenge. Conclusion The S-PRG filler containing resin cement can reduce mineral loss and promote remineralization of dentin substrate and has the potential to preserve dentin integrity and resist acidic attack. Clinical significance Self-adhesive resin cement containing S-PRG fillers maintained the surface integrity of dentin after exposure to 28 days of acidic challenge with a significant anti-demineralization effect.

Automated summary

The study found that resin cement containing S-PRG fillers can reduce mineral loss, promote remineralization, and has the potential to preserve dentin integrity and resist acidic attack.