Improved thermal and structural stabilities of LiNi0.6Co0.2Mn0.2O2 cathode by La2Zr2O7 multifunctional modification

Poor thermal stability and severe structural degradation of Ni-rich LiNi0.6Co0.2Mn0.2O2 (NCM622) cathode during the (de)lithiation process hinder its further application. As a typical thermal barrier material and ion conductor, La2Zr2O7 (LZO) was herein served as the multifunctional modification layer due to its excellent thermal stability, robust chemical stability, and prominent Li+ conductivity. Through optimizing the contents of LZO, 2 wt.% LZO-coated NCM622 (2LZO-NCM) displayed the much improved cycling stability (66.0% capacity retention at 0.2 degrees C after 300 cycles at 55 degrees C) and rate capability (73.0 mAh g(-1) at 5 degrees C) as compared with the pristine NCM622 (59.3%, 22.4 mAh g(-1)). An aging test, differential scanning calorimetry research, and kinetics analysis were conducted to unveil the improvement mechanism of electrochemical performances for 2LZO-NCM, mainly owing to the relieved structure degradation, boosted thermal stability, and enhanced electrochemical kinetics after LZO modification, synergistically contributing to the improved electrochemical performances. This work provides a universal avenue to enhance the thermal stability and electrochemical performances of the NCM622 cathode via employing the thermal barrier material as a coating layer, even in other cathodes beyond NCM622. Published under an exclusive license by AIP Publishing.

Automated summary

The modification of Ni-rich LiNi0.6Co0.2Mn0.2O2 (NCM622) with La2Zr2O7 (LZO) as a multifunctional layer significantly improves cycling stability and rate capability of the cathode material.