Nafion-Based Proton-Exchange Membranes Built on Cross-Linked Semi-Interpenetrating Polymer Networks between Poly(acrylic acid) and Poly(vinyl alcohol)

We report semi-interpenetrating polymer network (semi-IPN) membranes prepared easily from a cross-linked network using poly(acrylic acid) (PAA) and poly(vinyl alcohol) (PVA) with interpenetrated Nafion for both proton-exchange membrane fuel cell (PEMFC) and proton-exchange membrane water electrolyzer (PEMWE) applications. Thermal esterification between PAA and PVA induced three-dimensional cross-linking to improve mechanical toughness and reduce hydrogen crossover, while the hydrophilic nature of the PAA-PVA-based cross-linked matrix still enhanced the water uptake (WU) and hence conductivity of the Nafion penetrant. The semi-IPN membrane (NPP-95) composed of Nafion, PAA, and PVA with a ratio of 95:2.5:2.5 showed a hexagonal cylindrical morphology and improved thermal, mechanical, and dimensional stability compared to a recast Nafion membrane (re-Nafion). The membrane was also highly effective at managing water due to its low WU and high conductivity. Furthermore, its hydrogen permeability was 49.6% lower than that of re-Nafion under the actual fuel cell operating conditions (at 100% RH and 80 degrees C). NPP-95 exhibited significantly improved conductivity and PEMFC performance compared to re-Nafion with a current density of 1561 mA/cm(2) at a potential of 0.6 V and a peak power density of 1179 mW/cm(2). Furthermore, in the PEMWE performances, NPP-95 displayed about a 1.5-fold higher current density of 4310 mA/cm(2) at 2.0 V and much lower ohmic resistance than re-Nafion between 60 and 80 degrees C.

Automated summary

The semi-IPN membrane NPP-95, composed of Nafion, PAA, and PVA, exhibited excellent thermal, mechanical, and dimensional stability, as well as lower permeability and higher conductivity compared to re-Nafion. The membrane showed significantly improved water management and lower hydrogen crossover under actual fuel cell operating conditions. In both PEMFC and PEMWE applications, NPP-95 demonstrated higher current density and better performance than re-Nafion.