Designing Ultrasmall Carbon Nanospheres with Tailored Sizes and Textural Properties for High-Rate High-Energy Supercapacitors

Journal

ACS APPLIED MATERIALS & INTERFACES
Volume 13, Issue 28, Pages 32916-32929

Publisher

AMER CHEMICAL SOC
DOI: 10.1021/acsami.1c05816

Keywords

supercapacitors; carbon nanospheres; rate performance; energy density; low-temperature performance

Funding

  1. Natural Science and Engineering Research Council of Canada [RGPIN-2015-03815, RGPIN-2020-05546]

Ask authors/readers for more resources

The research demonstrates the efficient design of ultrasmall porous carbon nanospheres with tailored sizes and optimized intrasphere textural properties for high-rate high-energy super-capacitor application. Dual-step activation enlarges intrasphere micropores/mesopores, facilitating enhanced ion transports, and decreasing nanosphere size significantly improves the rate performance due to enhanced intrasphere ion transport. The optimum dual-step-activated carbon nanosphere sample shows high specific capacitances and outstanding high-rate capabilities in both aqueous and EMIMBF4 electrolytes.
The present work demonstrates the efficient design of ultrasmall porous carbon nanospheres with tailored sizes (5-40 nm in diameter) and optimized intrasphere textural properties for high-rate high-energy super-capacitor application. The carbon nanospheres are synthesized via a miniemulsion polymerization technique followed by KOH activation. It is shown that dual-step activation renders enlarged intrasphere micropores/ mesopores, facilitating enhanced ion transports. Meanwhile, a decrease in nanosphere size from 40 to 5 nm significantly improves the rate performance, demonstrating the pronounced size effects due to enhanced intrasphere ion transport. The optimum dual-step-activated carbon nanosphere sample with an average sphere size of 5 nm, ACNS5-2, shows the high specific capacitances along with outstanding high-rate capabilities in both aqueous (272 F g(-1) at 0.5 A g(-1) and 81.6% of retention at 200 A g(-1)) and EMIMBF4 (223 F g(-1) at 0.5 A g(-1) and 67.2% of retention at 100 A g(-1)) electrolytes in symmetrical two-electrode cells. In EMIMBF4, ACNS5-2 displays a high energy density of 48 Wh kg(-1) at a high power density of 14 kW kg(-1), suggesting excellent energy storage efficiency. Moreover, the performance of ACNS5-2 competes well with or is superior to some best-performing porous carbon-based materials reported in the literature for supercapacitor applications even at lowered temperatures (at -20 degrees C: 150 F g(-1) at 0.5 A g(-1) with a capacitance retention of 64% at 10 A g(-1)) and high mass loading (8 mg cm(-2): 205 F g(-1) at 0.5 A g(-1) with a capacitance retention of 64.5% at 20 A g(-1)). Our results, combined with structure-performance relationships, offer valuable guidelines for the rational design of carbon nanomaterials of optimum supercapacitive performances.

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.8
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available