Journal
CIRP JOURNAL OF MANUFACTURING SCIENCE AND TECHNOLOGY
Volume 33, Issue -, Pages 443-453Publisher
ELSEVIER
DOI: 10.1016/j.cirpj.2021.04.012
Keywords
Finite Element Analysis (FEA); Fused Deposition Modelling (FDM); Semi-crystalline polymers; Warpage; Simulation; 3D printing
Categories
Funding
- European Union's INTERREG VA Programme [INTVA/047]
- COMSOL
Ask authors/readers for more resources
This study investigates the impact of various printing parameters on residual stresses and warpage in semi-crystalline polymers during Fused Deposition Modelling (FDM). It is found that reducing layer thickness and changing raster pattern can effectively decrease part distortion, with simulation results showing good agreement with experimental results.
Residual stresses and warpage adversely affect the dimensional accuracy and performance of 3D-printed semi-crystalline polymers in Fused Deposition Modelling (FDM). One of the main challenges in FDM is to understand and relate the impact of printing conditions on part distortion for optimizing the 3D-printing process to achieve good print quality. Hence, the effect of various printing parameters, particularly print bed temperature, layer bonding, layer thickness and raster pattern, on built-up residual stresses and warpage is simulated in this work, by building a relationship between the crystallisation kinetics, viscoelastic and thermo-mechanical properties of the polymer in relation to changes in temperature during FDM using element activation in COMSOL. To the best of our knowledge, this is a novel approach for quantitative prediction of part distortion in FDM of semi-crystalline polymers under various printing conditions. Based on the simulation results, it is observed that a decrease in layer thickness from 0.5 mm to 0.1 mm results in an 89% drop in warpage and a reduction in residual stress of 24%. Applying a line raster pattern reduces warpage and residual stresses by 16% and 36%, respectively in comparison with a zigzag raster pattern. Very good agreement is observed between simulation and experimental results for warpage under various printing conditions. The results of this study can be used to predict and/or minimise part distortion in a semi-crystalline, 3D-printed polymer by simulating the effect of printing parameters on residual stresses during FDM. Crown Copyright (C) 2021