Thermal CO Oxidation and Photocatalytic CO2 Reduction over Bare and M-Al2O3 (M = Co, Ni, Cu, Rh, Pd, Ag, Ir, Pt, and Au) Cotton-Like Nanosheets

Aluminum oxide (Al2O3) has abundantly been used as a catalyst, and its catalytic activity has been tailored by loading transition metals. Herein, gamma-Al2O3 nanosheets were prepared by the solvothermal method, and transition metals (M = Co, Ni, Cu, Rh, Pd, Ag, Ir, Pt, and Au) were loaded onto the nanosheets. Big data sets of thermal CO oxidation and photocatalytic CO2 reduction activities were fully examined for the transition metal-loaded Al2O3 nanosheets. Their physicochemical properties were examined by scanning electron microscopy, high-resolution transmission electron microscopy, X-ray diffraction crystallography, and X-ray photoelectron spectroscopy. It was found that Rh, Pd, Ir, and Pt-loading showed a great enhancement in CO oxidation activity while other metals negated the activity of bare Al2O3 nanosheets. Rh-Al2O3 showed the lowest CO oxidation onset temperature of 172 degrees C, 201 degrees C lower than that of bare gamma-Al2O3. CO2 reduction experiments were also performed to show that CO, CH3OH, and CH4 were common products. Ag-Al2O3 nanosheets showed the highest performances with yields of 237.3 ppm for CO, 36.3 ppm for CH3OH, and 30.9 ppm for CH4, 2.2x, 1.2x, and 1.6x enhancements, respectively, compared with those for bare Al2O3. Hydrogen production was found to be maximized to 20.7 ppm during CO2 reduction for Rh-loaded Al2O3. The present unique pre-screening test results provided very useful information for the selection of transition metals on Al2O3-based energy and environmental catalysts.

Automated summary

In this study, gamma-Al2O3 nanosheets were prepared and loaded with various transition metals, and their catalytic activities in thermal CO oxidation and photocatalytic CO2 reduction were fully examined. It was found that Rh, Pd, Ir, and Pt-loading led to significant enhancement in CO oxidation activity. Ag-Al2O3 nanosheets showed the highest performance in CO2 reduction experiments.