The study investigated the cell toxicity of SiO2 nanoparticles under different calcination temperatures, times, and catalyst feed rates. Results showed that crystallization of the nanoparticles was influenced by the calcination temperature, with a negative correlation between crystallization and cell proliferation, and a positive correlation with cellular uptake.
Less attention had been paid to cell toxicity of the various synthesis methods of nanoparticles, this study investigated the effect of the calcination temperature(CT) on the crystallization of SiO2 nanoparticles(NPs), cell proliferation(CP), and cellular uptake(CU) in MRC-5. In this study, parameters were adjusted as CT(70-1000 degrees C), calcination time(2, 12, and 24 h), and catalyst feed rate(0.01, 0.05, and 0.1 mL.min(1)). CP was determined by the 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide(MTT) test after a 24-h exposure. The CU was achieved using ICP-MS. Results were analyzed using MATLAB2018. Results revealed that the size of synthesized particles was lower than 50 nm and, the XRD peak varied from 21 to 30 degrees during the increase in CT. FTIR spectra confirmed the existence of Si-O and Si-Cl bonds. The maximum level of crystallization was at 1000 degrees C. CP decreased with the rise in the concentration of NPs(p < 0.05), as well as an increase in feed rate. A positive relationship between increased crystallization and decreased CP(R = 0.78) was seen, while such a trend was not observed in calcination time. The suggested structure in this study was 4:10:1 with R-all = 0.97, R-test = 0.97, RMSE = 0.25, and MSE = 0.003. Furthermore, the CU rate increased with the rise in CT and calcination time. The maximum and minimum CU levels were related to NPs calcinated in 1000 degrees C-24 h and 350 degrees C-2 h, respectively. As a consequence, the most toxicity of SiO2 NPs was related to the crystalline NP. Therefore, the increase in CT and the calcination time were significant factors affecting on crystallization of SiO2 NPs, CP of lung cell, as well as CU of SiO2.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available