Journal
THERMOCHIMICA ACTA
Volume 699, Issue -, Pages -Publisher
ELSEVIER
DOI: 10.1016/j.tca.2020.178853
Keywords
Dicyclopentadiene petroleum resin; Thermal decomposition; Kinetics; Evolved gas analysis; Mechanism; TG-MS
Funding
- National Natural Science Foundation of China [21878056, 31560241]
- Key Laboratory of Petrochemical Resource Processing and Process Intensification Technology [2019Z002]
Ask authors/readers for more resources
The thermal decomposition behavior and kinetics of dicyclopentadiene petroleum resin (DPR) and hydrogenated dicyclopentadiene petroleum resin (HDPR) were investigated, revealing that DPR is easier to decompose and undergo repolymerization at high temperature environment, forming a cross-linked structure, whereas HDPR has a lower thermal mass loss rate and higher thermal structure stability.
The thermal decomposition behavior and kinetics of dicyclopentadiene petroleum resin (DPR) and hydrogenated dicyclopentadiene petroleum resin (HDPR) were extensively explored. Both resins had two complex overlapping pyrolysis stages. The activation energy of DPR pyrolysis varied between 79-236 kJ mol(-1). The pyrolysis of DPR mainly contained depolymerization accompanied by repolymerization. The main product was cyclopentadiene. By contrast, the initial pyrolysis rate of HDPR was relatively slow. The activation energy of HDPR pyrolysis ranged from 67-217 kJ mol(-1). The pyrolysis process of HDPR is mainly ring opening and dehydrogenation reaction. Alkenes, alkynes and hydrogen were its main products. These results indicate DPR was easy to decompose and part of the molecule was changed to cross-linked reticular structure by the repolymerization at high temperature environment. Compared with that, HDPR has lower thermal mass loss rate and higher thermal structure stability.