Two-step fabrication of thin film encapsulation using laser assisted chemical vapor deposition and laser assisted plasma enhanced chemical vapor deposition for long-lifetime organic light emitting diodes

A thin film encapsulation layer was fabricated through two-sequential chemical vapor deposition processes for organic light emitting diodes (OLEDs). The fabrication process consists of laser assisted chemical vapor deposition (LACVD) for the first silicon nitride layer and laser assisted plasma enhanced chemical vapor deposition (LAPECVD) for the second silicon nitride layer. While SiNx thin films fabricated by LAPECVD exhibits remarkable encapsulation characteristics, OLEDs underneath the encapsulation layer risk being damaged during the plasma generation process. In order to prevent damage from the plasma, LACVD was completed prior to the LAPECVD as a buffer layer so that the laser during LACVD did not damage the devices because there was no direct irradiation to the surface. This two-step thin film encapsulation was performed sequentially in one chamber, which reduced the process steps and increased fabrication time. The encapsulation was demonstrated on green phosphorescent OLEDs with I?V-L measurements and a lifetime test. The two-step encapsulation process alleviated the damage on the devices by 19.5% in external quantum efficiency compared to the single layer fabricated by plasma enhanced chemical vapor deposition. The lifetime was increased 3.59 times compared to the device without encapsulation. The composition of the SiNx thin films was analyzed through Fourier-transform infrared spectroscopy (FTIR). While the atomic bond in the layer fabricated by LACVD was too weak to be used in encapsulation, the layer fabricated by the two-step encapsulation did not reveal a Si?O bonding peak but did show a Si?N peak with strong atomic bonding.

Automated summary

A thin film encapsulation layer was fabricated using two sequential chemical vapor deposition processes to improve the stability and performance of organic light emitting diodes. The two-step encapsulation process, with LACVD as a buffer layer followed by LAPECVD as the main encapsulation layer, effectively alleviated the risk of plasma damaging the devices.