Journal
COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS
Volume 615, Issue -, Pages -Publisher
ELSEVIER
DOI: 10.1016/j.colsurfa.2020.126063
Keywords
Bismuth titanate; Graphitic carbon nitride; Hollow nanofibers; Heterostructure; Visible-light photocatalysis
Categories
Funding
- National Natural Science Foundation of China [21801091, 21902060]
- Outstanding Young Talents Fund Project of Jilin Provincial Department of Science and Technology [20190103117JH]
- Project of Jilin Provincial Department of Education [JJKH20191009KJ, JJKH20200242KJ, JJKH20190827KJ]
- Science and Technology Innovation Development Project of Jilin City [20190104169]
Ask authors/readers for more resources
The research successfully synthesized a novel g-C3N4/Bi4Ti3O12 hollow nanofiber composite through a convenient method, exhibiting excellent photocatalytic performance for the degradation of various pollutants under visible light. Among the samples prepared, CN/BTO-9 showed the best photocatalytic performance due to its unique structure, high specific surface area, and effective charge separation technology.
The exploration and development of effective and persistent visible-light-responsive photocatalysts for environmental remediation is regarded as one of the most challenging current research areas. Herein, a novel g-C3N4/Bi4Ti3O12 (CN/BTO-X; X = 6, 9 and 10.8) hollow nanofiber composite was fabricated through a convenient electrospinning/calcination technique, followed by thermal polymerisation. The SEM and TEM images showed that CN/BTO composite mainly comprised a hollow nanofiber morphology with a diameter of 110 +/- 20 nm. The XPS result confirmed the interfacial interaction between BTO and CN, implying the formation of a heterojunction between these components. Photocatalytic measurements revealed that the as-synthesized CN/BTO composite exhibited excellent and stable photocatalytic behaviour of dislodging multiple pollutants (including RhB, MO, TC and Cr (VI) etc.) with visible light (lambda > 420 nm). Among these prepared composites, the CN/BTO-9 sample exhibited the highest photocatalytic performance with the rate constants of 0.03064 min(-1) (TC), 0.11274 min(-1) (RhB), 0.04474 min(-1) (MO) and 0.01938 min(-1) (Cr(VI)), respectively. The outstanding catalytic performance was ascribed to the high specific surface area, improved visible-light adsorption, heterostructure of CN/BTO with strong oxidative ability and efficient separation of photoinduced charge carriers, and its unique hollow nanofiber structure. The active species-capturing experiments and ESR tests verified that h(+) and O-center dot(2)- were responsible for RhB/TC degradation. The mechanism accounting for the observed catalytic activities was discussed according to the band gap structure, DFT calculations and free radicals capture tests.