The tribocorrosion behaviour of YSZ coating deposited on stainless steel substrate in 3.5 wt% NaCl solution

The YSZ coating was applied to 304 stainless steel substrate by atmospheric plasma spraying technology, and its electrochemical and tribological properties in 3.5 wt% NaCl solution were studied. In electrochemistry, under the action of cathode and anode potential, observe the changes of corrosion current density and EIS before and after wear. The results show that the YSZ coating has a very low corrosion current density during wear and corrosion compared to 304 stainless steel, and after the condition of the anode potential is applied, the effect of friction on the electrochemical impedance of the YSZ coating is very low, while the 304 stainless steel Impedance performance decreases; In terms of tribology, the friction coefficient of 304 stainless steel in 3.5 wt% NaCl solution is easily affected by potential, and the friction coefficient of YSZ coating relative to 304 stainless steel only changes under high potential. As the potential increases, the material volume loss of 304 stainless steel and YSZ coating increases linearly. From the data, the volume loss caused by the corrosion and wear of 304 stainless steel is much higher than that of YSZ coating.

Automated summary

The YSZ coating has excellent electrochemical and tribological properties in 3.5 wt% NaCl solution when applied to a 304 stainless steel substrate, exhibiting low corrosion current density and friction coefficient. The friction coefficient only changes under high potential, and the material volume loss increases linearly with potential.